pc solid sheet/polycarbonate sheet/polycarbonate solid sheet
1.any colors can be available
2.thinkness1.5-16mm
3.UV cut
pc solid sheet/polycarbonate sheet/polycarbonate solid sheetPC Solid sheet standard size,weight and colorsRelated Product Searches:100% pure pc solid sheet,High Quality,pc solid sheet, pc corrugated sheet,ADLSS
Thickness | Standard Width | Length | Theoretical Weight | Standard Color |
mm | mm | m | Kg/sq.m. | |
1.5 | 1050;1220;1560;1820;2100 | Standard Length=30m,other size can be custom-made | 1.80 | Clear,Green,Dark brown,Lake blue,Opal,Royalblue,Gray,Red,ect.For large order,color can becustom-made |
1.8 | 2.16 | |||
2.2 | 2.64 | |||
2.7 | 3.24 | |||
3 | Size can be custom-made | 3.60 | ||
3.5 | 4.20 | |||
4 | 4.80 | |||
5 | 6.00 | |||
6 | 7.20 | |||
7 | 8.40 | |||
8 | 9.60 | |||
9 | 10.80 | |||
10 | 12.00 | |||
11 | 13.20 | |||
12 | 14.40 | |||
13 | 15.60 | |||
14 | 16.80 | |||
15 | 18.00 | |||
16 | 19.20 |
Properties | Experimental Condition(American Customary System) | ASTM Method (American Society of Testing Materials) | Unit--international System(American Customary System) | Values(American Customary System) |
Physical property | ||||
Density | D-1505 | g/cu.cm(lb/cu.ft) | 1.2(75) | |
Water content | 24h,23°C | D-570 | % | 0.15 |
Mechanical property | ||||
Tensional yield | 10mm/min(0.4in./min) | D-638 | Mpa(psi) | 65(9400) |
Ultimate tensile strength | 10mm/min(0.4in./min) | D-638 | Mpa(psi) | 60(8800) |
Yield strain | 10mm/min(0.4in./min) | D-638 | % | 6 |
Ultimate strain | 10mm/min(0.4in./min) | D-638 | % | >90 |
Stretching elastic coefficient | 10mm/min(0.4in./min) | D-638 | Mpa(psi) | 2000(290000) |
Bending coefficient | 1.3mm/min(0.052in./min) | D-790 | Mpa(psi) | 2600(380000) |
Bending force upon yielding | 1.3mm/min(0.052in./min) | D-790 | Mpa(psi) | 100(14500) |
Scrath-resistant load | 23°C(73°F) | D-256 | J/m(ft.lbf/in.) | 800(15) |
Charpy impact load | 23°C(73°F) | D-256 | J/m(ft.lbf/in.) | 800(15) |
Drop resistant ability | ISO-6603/1B | J(ft.lbf) | 158(117) | |
Rockwell hardness | D-785 | R scale/M scale | 125/75 | |
Thermal property | ||||
Long-term service temperature | °C(°F) | -75~100(-175~212) | ||
Short-term service temperature | °C(°F) | -75~120(-175~250) | ||
Heating deviating temperature | 1.82MPa(264psi) | D-648 | °C(°F) | 130(265) |
Vicat softening temperature | 1kg(2.2lb) | D-1525 | °C(°F) | 150(300) |
Linear thermal expansion coefficient | D-696 | 10-5/°C(10-5°F) | 6.5(3.6) | |
Thermo-conductivity | C-177 | W/m°K(Btu-in./hr-ft.2-°F) | 0.21(1.46) | |
Specific heat capacity | C-351 | kJ/kg°K(Btu/lb°F) | 1.26(0.31) | |
Optical performance | ||||
Ambiguity | D-1003 | % | <0.5 | |
Luminousness | D-1003 | % | 89 | |
Refraction rate | D-542 | 1.59 | ||
Yellowing index | D-1925 | |||
Notes:1.he experiment condition,unit and experiment numerical values in thes table presented by American standard are listed between brackets.2.The experiment results shown in this table are completely obtained in accordance with the experimental method of ASTM(American Society of Testing Materials),except for the results marked with "b",which is obtained by another experimental method.3.The experimental results given in thes table are closest to the properties of sheets of thickness 3mm(1/8 inch)(if the results are to be applied). |
100% pure pc solid sheet